Examples

  • German Cinematic Museum, Berlin, Sony Center

    German Cinematic Museum, Berlin, Sony Center

BARiT designer floors

Ageless aesthetics and manifold designs and grainings plead for BARiT Terrazzo coatings to fit out any impressive objects Terrazzo coatings of high quality unite the features of no joints and high mechanical and chemical resistance to loads.
Deutsches Filmmuseum, Berlin, Sony Center
Deutsches Filmmuseum, Berlin, Sony Center

BARiT SEALS are perfect for accentuating the loft-like character of a mineral subfloor. Polished screed is transformed into genuine designer floors through the transparent BARiT SEALS.

BARiT SEALS are used to create designer floors with a transparent or coloured appearance.

 

Thus, it is protected against the ingress of contaminants and dust collection caused by abrasion is prevented. Similarly, a sealed floor is water-resistant and can be cleaned and maintained more easily.

 

A coloured coating creates a lively habitat; a transparent order creates a purist concrete look. The colour range is supplemented by various degrees of gloss.

Quick Info

  • seamless
  • dust binding
  • mechanically and chemically resistant
  • low abrasion
  • easy to clean
  • low emissions according to AgBB
  • declared according to DGNB and LEED

Optics

BARiT SEALS can be applied transparently or pigmented, in satin or matte, depending on the system used for application. Different degrees of gloss are also possible: Matte, satin, glossy.

RAL 7047
RAL 7047
telegrey
RAL 7012
RAL 7012
basalt grey
RAL 9011
RAL 9011
graphite black

Properties

Type: EXW, pigmented or transparent
The pigmented EXW-Sealant is a two-component system based on a colour pigmented, water-dilutable, epoxy resin.
Based on "Building green" this surface coating has achieved 7.5 out of a possible 10 points for LEED and DGNB. It is extremely low emission, solvent free and therefore emits very minimal odor during application. Full overage with the sealant is achieved by repeated applications. After 2-3 coats, the layer's thickness can be measured at up to 0.5 mm.

Type: D1-55
BARiT Sealant - Type: D1-55, is a transparent, high-gloss, two-component system based on polyurethane resin, which is characterized by good light resistance as well as chemical resistance.

Type: DW11
BARiT Sealant - Type: DW11, is a transparent or pigmented, matte, two-component system based on polyurethane resin, which is characterized by good light resistance as well as chemical resistance.
BARiT Sealants are water, oil and petrol resistant, as well as resistant to a variety of alkalis, diluted acids and salt solutions.
For high temperature exposure, BARiT Sealants can handle temperatures between 95° and 150 °C temporarily.

Type SEAL
Working under conditions of EXW:
  • air humidity
  • residual moisture of the ground
  • ground temperature min.
  • ground temperature max.
 
  • 40 - 85%
  • 4 - 10 %
  • 10 °C
  • 22 °C
Curing time at 20°C EXW:
  • not sticky
  • walking admissible
  • final hardness
  • mechanical stability
 
  • after 4 hours
  • after 16 hours
  • after 7 days
  • after 7 days
Working under conditions of D1-55:
  • air humidity
  • residual moisture of the ground
  • ground temperature min.
  • ground temperature max.
 
  • 40 - 85%
  • 4 - 10 %
  • 10 °C
  • 22 °C
Curing time at 20°C D1-55:
  • not sticky
  • walking admissible
  • final hardness
  • mechanical stability
 
  • after 5 hours
  • after 8 hours
  • after 4 days
  • after 24 hours
Working under conditions of DW11:
  • air humidity
  • residual moisture of the ground
  • ground temperature min.
  • ground temperature max.
 
  • 40 - 85%
  • 4 - 10 %
  • 10 °C
  • 22 °C
Curing time at 20°C DW11:
  • not sticky
  • walking admissible
  • final hardness
  • mechanical stability
 
  • after 5 hours
  • after 8 hours
  • after 4 days
  • after 24 hours
TYPE EXW D1-55 DW11
Binding agent 2-K-EP-resin, emulsified water 2-K-PUR-resin, in organ. solvents 2-K-PUR-resin, dispersed water
Consumption/m² 100-150 g / process 70-100 g / process 70-100 g / process
Colour shade colourless / pigmented colourless / pigmented colourless / pigmented
Grade of gloss silk gloss high gloss mat / silk mat
Bending tensile strength DIN 1164** - - -
Compression strength DIN 1164** - - -
Adhesive pull strength DIN EN 24624 > 1 N/mm² > 1 N/mm² > 1 N/mm²
Light-fastness not UV resistant conditionally resisting to UV conditionally resisting to UV
DGNB / LEED declaration 7,5 Point - declaration 7,5 Point
VOC Emission Meets the requirements of AgBB Meets the requirements of AgBB Meets the requirements of AgBB
Light-Temperature resistant 95 °C temporarily / 70 °C consistently 150 °C temporarily / 120 °C consistently 150 °C temporarily / 120 °C consistently
Chemical resistance to resistance list and self test to resistance list and self test to resistance list and self test
Cleaning BARiT Cleaner* BARiT Cleaner* BARiT Cleaner*
** with prism method - according to AGI Worksheet A 81 and BEB Worksheets KH 5
* according to cleaning and care instructions