Elastic B 65 | BARiT


  • Geschwister Seipp GbR

    Geschwister Seipp GbR

  • Guardini School Munich

    Guardini School Munich

  • VW Autostadt - Pavillon, Wolfsburg

    VW Autostadt - Pavillon, Wolfsburg

  • Penthouse, Esslingen

    Penthouse, Esslingen

BARiT designer floors

Ageless aesthetics and manifold designs and grainings plead for BARiT Terrazzo coatings to fit out any impressive objects Terrazzo coatings of high quality unite the features of no joints and high mechanical and chemical resistance to loads.
VW Markenpavillon, Wolfsburg
VW Markenpavillon, Wolfsburg

The BARiT ELASTIC B 65 combines the highest standards of design, quality, feel, spirit of the time and style.


Additionally, ELASTIC B 65 meets high functional requirements, such as fade-resistance and UV stability. With the creative variety of flooring colours the architecture receives a style element to achieve holistic, seamless surfaces.

The elasticity of the flooring provides good damping properties, which makes standing and walking on this flooring more comfortable.

Quick Info

  • crack-bridging
  • seamless
  • non-slip matte finish in accordance with BGR 181, R 9, R 11
  • mechanically and chemically resistant
  • declared according to DGNB and LEED
  • low abrasion
  • fire protection class Cfl-s1
  • low emissions according to AGBB
  • easy to clean and disinfect


ELASTIC B 65 can be installed in a matte or satin finish based on BARiT colour charts. Qualitative benefits such as high-quality colour stability and intensity characterize ELASTIC B65 as a designer floor. This coating surface is available in a large colour spectrum of RAL colours. A matte surface with slip-resistance class R 9 provides for sure-footed walking.

Specialized colours are available for areas over 200m².

RAL 9002
RAL 9002
grey white
RAL 7012
RAL 7012
basalt grey


The ELASTIC B 65 is a two-coponent, low emission, solvent-free, polyurethane resin. Excelling in factors for "Building green" this surface coating has achieved 7.5 out of a possible 10 points for LEED and DGNB in environment quality. It can be installed on top of calcium-sulfate based false and subflooring, cement as well as anhydrite flooring, and especially on heated flooring.
The synthesis between profession laying technology and the quality of the material provide for a low abrasion coating that offers good mechanical strength. The coating is installed in a layer 2 - 3 mm thickness. ELASTIC B 65 has a high chemical resistance against salts, urine, cooking oils and food acids. The dense surface is water-repellent, dirt resistant and can be easily cleaned.

Compression strength DIN 1164** elastic
Adhesive pull strength DIN EN 24624 > 1,0 N/mm²
Light-fastness resisting to UV with finish
VOC Emission Meets the requirements of AgBB
Flash point > 100 °C
Anti-slip Class DIN 51130 R9, R11
Colour shade BARiT card of colours
Fire behaviour DIN EN 13501-1 Cfl-s1, hardly inflammable
Grade of gloss gloss/silk gloss/mat
Bending tensile strength DIN 1164** elastic
Adhesion strength on concrete > 2 N/mm2 (fracture on concrete)
crack bridging according to DIN EN 1062-7
  • with approx. 1.5 mm thickness
test temperature: + 23 °C
  • 1.0 mm
Consumption/m² 1,4 kg/mm
Light-Temperature resistance 120 °C temporarily / 40 °C consistently
Chemical resistance to resistance list and self test
Binding agent 2-K-PUR-resin
Working under conditions of:
  • ground temperature max.
  • air humidity
  • residual moisture of the ground
  • ground temperature min.
  • 22 °C
  • 40 - 65%| <80%
  • < 3 %
  • 18 °C
ultimate tensile strength according to DIN EN ISO 527
  • Tension
  • Elogation
test temperature: + 23 °C
  • 6.0 MPa
  • 69,2 %
Curing time at 20°C:
  • mechanical stability
  • walking admissible
  • not sticky
  • final hardness
  • after 7 days
  • after 16-24 hours / 24 hours
  • after 8-10 hours / 16 hours
  • after 7 days
Cleaning BARiT Cleaner*
DGNB/ LEED declaration 7,5 point
** with prism method - according to AGI Worksheet A 81 and BEB Worksheets KH 5
* according to cleaning and care instructions