Ageless aesthetics and manifold designs and grainings plead for BARiT Terrazzo coatings to fit out any impressive objects Terrazzo coatings of high quality unite the features of no joints and high mechanical and chemical resistance to loads.
Hypovereinsbank, München
Hypovereinsbank, München

Inspired by the classic terrazzo Veneziani, BARiT developed an epoxy resin-bound terrazzo. This flooring is grinded several times in order to achieve the particularly elegant appearance.


The TERRAZZO-VENEZIANI offers all creative possibilities for the restoration of historic buildings and for modern design concepts through the variety of coloured aggregates. With craftsmanship inlaid work, moulding and logos can be integrated for a defining look.

Quick Info

  • seamless
  • aesthetic
  • slip-resistant in accordance with BGR 181 R 9
  • chemical and mechanical stability
  • suitable for wheelchairs
  • easy to clean and disinfect
  • Fire classification Bfl-s1


The ideal starting point for the terrazzo look - including inlays, beading (friezes) or logos provided for by BARiT craftsmanship. Careful grinding of the surface provides for a truly noble terrazzo appearance.

RAL 9010
RAL 9010
pure white, Terralith, sanded
RAL 1013
RAL 1013
oyster white, Terralith, sanded
RAL 7016
RAL 7016
anthracite grey


TERRAZZO-VENEZIANI consists of epoxy resin and granules, installed in a layer 8-10 mm thick. Ribboned tracks made from stainless steel or aluminum incorporate ornaments and optical structures. The high wear resistance of TERRAZZO-VENEZIANI makes it suitable for installation in mechanically stressed and high traffic areas. This covering is installed without any joints or edges, eliminating any hazards for tripping. Due to its seamless surface, TERRAZZO-VENEZIANI is easy to clean and maintain.
It can be installed on top of calcium-sulfate based false and subflooring, cement as well as anhydrite flooring, and especially on heated flooring.

Consumption/m² 2 kg/mm
Light-Temperature resistance 100 °C temporarily / -30 °C to +70 °C consistently
Anti-slip Class DIN 51130 R9, R11
Grade of gloss silk gloss or mat
Bending tensile strength DIN 1164** > 10 N/mm²
Solid matters 100 %
Fillers Granulates
Compression strength DIN 1164** > 40 N/mm²
Light-fastness conditionally resisting to UV
Flash point > 100 °C
Fire behaviour DIN EN 13501-1 Bfl-s1, hardly inflammable
Barefoot Suitability DIN 51097 B and C
Grain BARiT card of grains
Adhesive pull strength DIN EN 24624 > 1,0 N/mm²
Working under conditions of:
  • residual moisture of the ground
  • ground temperature min.
  • air humidity
  • ground temperature max.
  • < 3 %
  • 18 °C
  • 40 - 85%
  • 22 °C
VOC Emission Meets the requirements of AgBB
Chemical resistance to resistance list and self test
Curing time at 20°C:
  • not sticky
  • walking admissible
  • final hardness
  • mechanical stability
  • after 12 hours
  • after 16 hours
  • after 7 days
  • after 7 days fully capable of bearing
Cleaning BARiT Cleaner*
Binding agent EP-resin